0.013000 	 6.376145
0.019200 	 6.481170
0.050000 	 6.967157
0.100000 	 7.771285
0.200000 	 9.419484
0.000000 	 6.123399

V/g = 16.34
R^2 = 0.99978

LOAD/UNLOAD SPEED: 20um/s
MAX LOAD = 1mN

SNAP FROZEN IN DRY ICE + ISOPROPANOL BATH. RHEOLOGY WAS PERFORMED FIRST, THEN CAT.
***OBSERVATION: THESE SAMPLES ARE VERY OBVIOUSLY DRIED OUT. SOME OF THEM HAVE TROUBLE STAYING FLAT. SOME SAMPLES ARE CURLING UP ON THE SIDES, PROBABLY DUE TO DEHYDRATION.


calib	0
A1-t1	-2206.5
A1-t2	-2240
A1-t3	-2487
B1-t1	-2442
B1-t2	-2218
B1-t3	-1769.5
A2-t1	-2404
A2-t2	-2613.5
A2-t3	-2492
B2-t1	-2591.5
B2-t2	-2274
B2-t3	-2466
C2-t1	-2363
C2-t2	-2276
C2-t3	-2265.5
B4-t1	-2164
B4-t2	-2277.5
B4-t3	-2035
B5-t1	-2321.5
B5-t2	-2564
B5-t3	-2591.5
C5-t1	-
C5-t2	-
C5-t3	-
B5-t1	-
B5-t2	-
B5-t3	-


"SLOW-FROZEN" IN THE -80C FREEZER. CAT WAS PERFORMED FIRST, THEN RHEOLOGY.

A3-t1	-7977.5	Sample is very thick, looks like rheology was not performed on this one
A3-t2	-8585
A3-t3	-8114
B3-t1	-2779
B3-t2	-2563
B3-t3	-2626.5
C3-t1	-2548.5
C3-t2	-2058
C3-t3	-1778
A4-t1	-2957
A4-t2	-2717
A4-t3	-2890
C4-t1	-1790
C4-t2	-1949
C4-t3	-2442
A6-t1	-2503
A6-t2	-2284
A6-t3	-2196
B6-t1	-2238
B6-t2	-2016.5
B6-t3	-2202
C6-t1	-1873.5
C6-t2	-2057
C6-t3	-2561
A7-t1	-2752
A7-t2	-2666
A7-t3	-1840
B7-t1	-2107
B7-t2	-2157
B7-t3	-2552.5